Aluminium Pipe
Trident Enterprises are among the pre-eminent organizations, involved in manufacturers, suppliers, stockists and exporter Aluminium Pipe. Available in different lengths, thicknesses and sizes, these Aluminium Pipe are widely demanded by various industries like food & beverage, chemical, petrochemical, pharmaceutical and cosmetics. In addition to this, we provide tailor-made solution for all our offered Aluminium Pipe as per customers’ requirements.
What is Aluminium?
Aluminium (or aluminum; see spelling differences) is a chemical element in the boron group with symbol Al and atomic number 13. It is a silvery-white, soft, nonmagnetic, ductile metal. Aluminium is the third most abundant element (after oxygen and silicon), and the most abundant metal in the Earth's crust. It makes up about 8% by weight of the Earth's solid surface. Aluminium metal is so chemically reactive that native specimens are rare and limited to extreme reducing environments. Instead, it is found combined in over 270 different minerals.The chief ore of aluminium is bauxite.Aluminium is remarkable for the metal's low density and for its ability to resist corrosion due to the phenomenon of passivation. Structural components made from aluminium and its alloys are vital to the aerospace industry and are important in other areas of transportation and structural materials. The most useful compounds of aluminium, at least on a weight basis, are the oxides and sulfates.
Despite its prevalence in the environment, no known form of life uses aluminium salts metabolically. In keeping with its pervasiveness, aluminium is well tolerated by plants and animals. Owing to their prevalence, potential beneficial (or otherwise) biological roles of aluminium compounds are of continuing interest.
| Type | Aluminium Pipe |
| Standards | ASME SB241, ASTM B210, WWW-T-700/5, ASTM B221, ASTM B241, ASTM B429, AMS-QQ-A-200/8, MIL-DTL-25995 Type A, ASTM B221, ASTM B241, ASTM B429, AMS-QQ-A-200/9 |
| Grade | 5086, 5083, 6061, 60630 |
| Wall Thickness | 0.2~5.0mm |
| Length | 200~6000mm |
| Outer Diameter | 1.0~150mm |
| Test Certificates | Manufacturer Test Certificate as per EN 10204 / 3.1B, Raw Materials Certificate, 100% Radiography Test Report, Third Party Inspection Report |
Chemical Composition
Component |
Amount (wt.%) |
Aluminium |
Balance |
Magnesium |
0.8-1.2 |
Silicon |
0.4 – 0.8 |
Iron |
Max. 0.7 |
Copper |
0.15-0.40 |
Zinc |
Max. 0.25 |
Titanium |
Max. 0.15 |
Manganese |
Max. 0.15 |
Chromium |
0.04-0.35 |
Others |
0.05 |
Mechanical Properties
Temper |
Ultimate Tensile Strength (MPa) |
0.2% Proof Stress (MPa) |
Brinell Hardness (500kg load, 10mm ball) |
Elongation 50mm dia (%) |
0 |
110-152 |
65-110 |
30-33 |
14-16 |
T1 |
180 |
95-96 |
|
16 |
T4 |
179 min |
110 min |
|
|
T6 |
260-310 |
240-276 |
95-97 |
9-13 |
Physical Property
Treatment |
Definition |
F |
As fabricated |
0 |
Annealed to obtain lower strength temper |
T1 |
Cooled from an elevated shaping process and naturally aged1 |
T4, T4511 |
Solution heat treated and naturally aged2,3 |
T51 |
Cooled from an elevated shaping process and artificially aged |
T6, T6511 |
Solution heat treated and artificially aged2,3 |
Note:
1. This designation applies to products which are not cold worked after cooling from an elevated temperature shaping process, or in which the effect of cold work in flattening or straightening has no effect on mechanical properties
2. This designation applies to products which are not cold worked after solution heat-treated, or in which the effect of cold work in flattening or straightening has no effect on mechanical properties
3. This designation applies to products which are not cold worked after solution heat-treatment, or in which the effect of cold work in flattening or straightening does not effect mechanical properties.